The fique is a plant typical of the Colombian Andes, from which relatively common items are fabricated. One of these is woven fabric extensively applied in sackcloths. The mechanical strength of fique fabric have motivated recent investigations on possible reinforcement of polymer matrix composites. For this purpose its thermo-mechanical behavior was unveiled. In particular, dynamic mechanical analysis (DMA) of fique fabric reinforced polyester matrix composites disclosed improved viscoelastic behavior in association with change in the glass transition temperature. The present work extends this investigation to epoxy matrix, which is one of the most employed thermoset polymer for composite matrix. Fique fabric volumetric fractions of up to 50% are for the first time incorporated into epoxy composites. It was found that these incorporations significantly increased the viscoelastic stiffness of the composite, given by the storage modulus (E’), in the temperature interval from -50 to 170°C. An accentuated softening in viscoelastic stiffness was revealed for all composites above 75°C. Peaks in both the loss modulus (E”) and tangent delta (tan δ), respectively associated with the lower and upper limits of the glass transition temperature, were shifted towards higher temperatures with increasing amount of fique fabric.

Waste incorporation into clay ceramic is a worldwide accepted recycling procedure for environmentally friendly reuse of spent industrial materials. In the present work a clay ceramic from the city of Campos dos Goytacazes, Brazil, was, for the first time, investigated with different amounts, up to 10 wt%, of a solid waste generated from the “Sulfatreat” natural gas treatment process. Both the waste and the incorporated ceramic were characterized by X-ray fluorescence and X-ray diffraction as well as vibratory sieving, gas chromatography and sedimentation method. Ceramic samples were prepared by uniaxial pressing at 18 MPa and sintered at 850°C. Physical and mechanical properties of these ceramics such as linear shrinkage, apparent density, water absorption and flexural strength were evaluated. Microstructure of the incorporated ceramics was analyzed by optical microscopy. The results showed that, within the standard deviation, the linear shrinkage and apparent density of the clay ceramic were not affected by the waste incorporation. However, the water absorption is benefitted, by decreasing above 5 wt% incorporation, while the flexural strength is impaired for any incorporated amount. Porosity and larger waste particles observed in microstructure are proposed reasons for these advantages and shortcomings.

The growing interest in natural lignocellulosic fibers (NLFs) is associated not only with environmental benefits but also with technical, economical and social advantages. Among the NLFs, the coir fiber and pineapple leaf fiber (PALF) are low-cost and widely available waste materials. The present work investigated the dynamic mechanical properties, by means of DMA tests, of these two different fibers as reinforcement of epoxy matrix composites. The influence on DMA properties of composites by the volume fraction and the configuration form, mat or aligned coir fiber, were also evaluated. The results showed higher E’ and E” moduli values and an increase in Tg with the incorporation of PALF in epoxy matrix, which indicate a superior dynamic mechanical properties for this composite in comparison to the neat epoxy resin. The experimental data also revealed a stronger interfacial interaction of PALF/epoxy when compared to coir fiber/epoxy. It was also found a lower tan δ value exhibited by higher volume fractions of aligned coir fibers in epoxy matrix.

Stainless steels are well known by their corrosion resistance. The austenitic types, in particular, are also applied as structural components in engineering systems operating at high temperatures such as nuclear reactors, petrochemical furnaces and turbines. For these applications operational temperatures may go up to 800ºC. Under constant load applications the main mechanism of failure, which would limit the material's life, is creep. In the present work creep parameters were evaluated in the high temperature interval of 600 to 800ºC for an AISI 316 austenitic stainless steel. Dislocation substructures were observed by transmission electron microscopy in creep ruptured specimens. Two distinct mechanisms of dynamic strain aging and dynamic recovery associated with different values for the power law exponent n and the Arrhenius activation energy Q for creep were verified below and above 700ºC, respectively.

Multilayered armor systems (MAS) composed of relatively lighter materials with capacity to provide personal ballistic protection are being extensively investigated and used in armor vests. A typical MAS to stand high impact energy 7.62 mm bullet has a front ceramic followed by an aramid fabric laminate, such as Kevlar™. Since both the army and municipal police personnel might need to wear an armor vest, a large number of vests needs to be supplied. In the case of Kevlar™, one of the most expensive MAS material with an expiration time of 5 years, the possibility of its replacement by an equally ballistic efficient low cost material and more durable could be a relevant economical advantage. Natural fibers composites have recently been investigated as possible alternatives for Kevlar™. In particular, the fiber extracted from the coconut fruit, known as coir fiber, normally disposed as waste, could be a low cost material for this purpose. Therefore, the present work investigated the possibility of using coir fiber mantle, with different volume fraction, reinforcing epoxy composites as MAS second layer. It was found that 30 vol% of coir fiber composite displayed similar ballistic performance as compared to Kevlar™ with substantial economical advantage.

Multilayered armors with a front ceramic followed by aramid fabric (Kevlar™) are currently used against high velocity ammunition. In these armors, a front ceramic layer that shatters and spalls the bullet is followed by an intermediate layer, usually plies of aramid fabric, which dissipates both the bullet and ceramic fragments energy. In the present work, the intermediate aramid fabric layer was replaced by an equal thickness layer of 30 vol% jute fabric reinforced epoxy composite. Ballistic impact test with 7.62 caliber ammunition revealed that both the plain epoxy and the jute fabric composite have a relatively similar performance of the Kevlar™ and also attended the NIJ standard for body protection. The energy dissipation mechanisms of jute fabric composite were analyzed by scanning electron microscopy and found to be the rupture of the brittle epoxy matrix as well as the interaction of the jute fibers with the post-impact fragments. This latter is the same mechanism recently disclosed for aramid fabric. However, the lightness and lower cost of the jute fabric composite are additional advantages that favor its substitution for the aramid fabric.